دانلود مقاله Synthesis of High SolidدرContent Anisotropic Nanoparticles by Cosurfactant Free Microemulsion Polymerization با wo
دانلود مقاله Synthesis of High SolidدرContent Anisotropic Nanoparticles by Cosurfactant Free Microemulsion Polymerization با word دارای 4 صفحه می باشد و دارای تنظیمات در microsoft word می باشد و آماده پرینت یا چاپ است
فایل ورد دانلود مقاله Synthesis of High SolidدرContent Anisotropic Nanoparticles by Cosurfactant Free Microemulsion Polymerization با word کاملا فرمت بندی و تنظیم شده در استاندارد دانشگاه و مراکز دولتی می باشد.
این پروژه توسط مرکز مرکز پروژه های دانشجویی آماده و تنظیم شده است
توجه : در صورت مشاهده بهم ریختگی احتمالی در متون زیر ،دلیل ان کپی کردن این مطالب از داخل فایل ورد می باشد و در فایل اصلی دانلود مقاله Synthesis of High SolidدرContent Anisotropic Nanoparticles by Cosurfactant Free Microemulsion Polymerization با word،به هیچ وجه بهم ریختگی وجود ندارد
بخشی از متن دانلود مقاله Synthesis of High SolidدرContent Anisotropic Nanoparticles by Cosurfactant Free Microemulsion Polymerization با word :
سال انتشار: 1388
محل انتشار: ششمین کنگره بین المللی مهندسی شیمی
تعداد صفحات: 4
چکیده:
The objective of this study was to produce the finest anisotrpic nano-particles through microemulsion polymerization. For this purpose we tried to develop a process, which yields a high solid content (HSC) and properly stable latex, despite the absence of co-surfactant. It is also considered that for being functional in the further applications, the resulting seed particles must be less than 50 nm in diameter. To achieve this goal, effect of variables such as surfactant and monomer concentrations and temperature on number average particle diameter was investigated. The HSC seed latex showed 32.3 nm of average particle diameter with the solid content of 25%, although other experiments with lower solid contents yielded smaller particles. These particles were later swelled by MMA monomer to form polystyrene/poly methyl methacrylate (PS/PMMA) interpenetrating polymer networks (IPNs). The consequent anisotropy was denoted to phase separation of second stage monomer from seed particle during the swelling and polymerization period. Other than chemical anisotropy of immiscible polymer pairs, reaction temperature and crosslink density are the most influential parameters on the final particle morphology. The average diameters of anisotropic particles were always smaller than 100 nm.